An experimental investigation of the surface topography, nanoindentation hardness, and nanowear characteristics of carbon thin films was conducted using atomic force and point contact microscopy. Hydrogenated carbon films of thickness 5, 10, and 25 nm were synthesized using a sputtering technique. Atomic force microscopy images obtained with silicon nitride tips of nominal radius less than 20 nm demonstrated that the carbon films possessed very similar surface topographies and root-mean-square roughness values in the range of 0.7–1.1 nm. Nanoindentation and nanowear experiments performed with diamond tips of radius equal to about 20 nm revealed a significant enhancement of the hardness and wear resistance with increasing film thickness. High-resolution surface imaging indicated that plastic flow was the dominant deformation process in the nanoindentation experiments. The carbon wear behavior was strongly influenced by variations in the film thickness, normal load, and number of scanning cycles. For a given film thickness, increasing the load caused the transition from an atomic-scale wear process, characterized by asperity deformation and fracture, to severe wear consisting of plowing and cutting of the carbon films. Both the critical load and scanning time for severe wear increased with film thickness. Below the critical load, the wear rate decreased with further scanning and the amount of material worn off was negligibly small, while above the critical load the wear rate increased significantly resulting in the rapid removal of carbon. The observed behavior and trends are in good qualitative agreement with the results of other experimental and contact mechanics studies.

1.
Alley
R. L.
,
Komvopoulos
K.
, and
Howe
R. T.
,
1994
, “
Self-Assembled Monolayer Film for Enhanced Imaging of Rough Surfaces with Atomic Force Microscopy
,”
J. Appl. Phys.
, Vol.
76
, No.
10
, pp.
5731
5737
.
2.
Bhattacharya
A. K.
, and
Nix
W. D.
,
1988
, “
Analysis of Elastic and Plastic Deformation Associated With Indentation Testing of Thin Films on Substrates
,”
Int. J. Solids Structures
, Vol.
24
, No.
12
, pp.
1287
1298
.
3.
Binnig
G.
,
Quate
C. F.
, and
Gerber
C.
,
1986
, “
Atomic Force Microscope
,”
Phys. Rev. Lett.
, Vol.
56
, No.
9
, pp.
930
933
.
4.
Kaneko
R.
,
Nonaka
K.
, and
Yasuda
K.
,
1988
, “
Summary Abstract-Scanning Tunneling Microscopy and Atomic Force Microscopy for Microtribology
,”
J. Vac. Sci. Technol. A
, Vol.
6
, No.
2
, pp.
291
292
.
5.
Kaneko, R., Oguchi, S., Miyamoto, T., Andoh, Y., and Miyake, S., 1990, “Micro-Tribology for Magnetic Recording,” Tribology and Mechanics of Magnetic Storage Systems, Vol. VII, STLE Special Publication SP-29, pp. 31–34.
6.
Kaneko
R.
, and
Hamada
E.
,
1993
, “
Microwear Processes of Polymer Surfaces
,”
Wear
, Vol.
162-164
, pp.
370
377
.
7.
Komvopoulos
K.
,
Saka
N.
, and
Suh
N. P.
,
1987
, “
The Role of Hard Layers in Lubricated and Dry Sliding
,”
ASME JOURNAL OF TRIBOLOGY
, Vol.
109
, No.
2
, pp.
223
231
.
8.
Komvopoulos
K.
,
1989
, “
Elastic-Plastic Finite Element Analysis of Indented Layered Media
,”
ASME JOURNAL OF TRIBOLOGY
, Vol.
111
, No.
3
, pp.
430
439
.
9.
Kral, E. R., Komvopoulos, K., and Bogy, D. B., 1996, “Hardness of Thin-Film Media: Scratch Experiments and Finite Element Simulations,” ASME JOURNAL OF TRIBOLOGY, Vol. 118, No. 1.
10.
Lu
C. J.
,
Bogy
D.
, and
Kaneko
R.
,
1994
, “
Nanoindentation Hardness Tests Using a Point Contact Microscope
,”
ASME JOURNAL OF TRIBOLOGY
, Vol.
116
, No,
1
, pp.
175
180
.
11.
Mate
C. M.
,
McClelland
G. M.
,
Erlandsson
R.
, and
Chiang
S.
,
1987
, “
Atomic-Scale Friction of a Tungsten Tip on a Graphite Surface
,”
Phys. Rev. Lett.
, Vol.
59
, No.
17
, pp.
1942
1945
.
12.
Miyake
S.
,
Kaneko
R.
,
Kikuya
Y.
, and
Sugimoto
I.
,
1991
, “
Micro-Tri-bological Studies on Fluorinated Carbon Films
,”
ASME JOURNAL OF TRIBOLOGY
, Vol.
113
, No.
2
, pp.
384
389
.
13.
Miyake
S.
,
Watanabe
S.
,
Murakawa
M.
,
Kaneko
R.
, and
Miyamoto
T.
,
1992
, “
Tribological Study of Cubic Boron Nitride Film
,”
Thin Solid Films
, Vol.
212
, pp.
262
266
.
14.
Miyamoto
T.
,
Kaneko
R.
, and
Ando
Y.
,
1990
, “
Interaction Force Between Thin Film Disk Media and Elastic Solids Investigated by Atomic Force Microscope
,”
ASME JOURNAL OF TRIBOLOGY
, Vol.
112
, No.
3
, pp.
567
572
.
15.
Miyamoto
T.
,
Kaneko
R.
, and
Miyake
S.
,
1991
, “
Tribological Characteristics of Amorphous Carbon Films Investigated by Point Contact Microscopy
,”
J. Vac. Sci. Technol. B
, Vol.
9
, No.
2
, pp.
1336
1339
.
16.
Miyamoto
T.
,
Miyake
S.
, and
Kaneko
R.
,
1993
, “
Wear Resistance of C+-implanted Silicon Investigated by Scanning Probe Microscopy
,”
Wear
, Vol.
162-164
, pp.
733
738
.
This content is only available via PDF.
You do not currently have access to this content.