The fracture behavior of thick-walled nuclear vessels is considered for the case of a radiation-induced toughness gradient through the wall which characteristically results from neutron attenuation by the wall material itself. Fracture-safe design analyses based on linear elastic formulations or extrapolations of these formulations to the elastic-plastic regime are not sufficiently developed to characterize the integrated behavior of a wall whose toughness can range from brittle at the inner surface to highly ductile at the outer surface. Solutions to the problem in the foreseeable future will be obtained only by experimental means. The present approach uses the Fracture Analysis Diagram (FAD) together with a new interpretative method for fracture extension resistance based on modified dynamic tear specimens as the tools for gradient assessments. With these techniques the significance of the toughness gradient through the wall is assessed in terms of thick section mechanical constraint, and fracture characteristics of the complete wall are predicted. Characterization of a hypothetical 8-in. vessel wall is based on measured through-thickness fluence levels; this behavior is correlated with fracture toughness degradation for steels of varying sensitivity to irradiation using the FAD. This analysis indicates that major portions of the vessel wall remain above the FTE temperature, which dictates yield stress loading requirements for fracture, when the wall temperature is maintained at the limiting value, NDT + 60 deg F, for the inside surface as suggested by current AEC criteria. Fracture extension resistance measurements based on data from a 3-in. thick plate having a metallurgically induced toughness gradient suggest that nuclear vessels with analogous gradients will not fracture in an unstable fashion and will not generate missiles capable of breaching the containment system. Additional research is necessary to fully develop the approach for application to the individual reactor vessel.
Skip Nav Destination
Article navigation
November 1971
This article was originally published in
Journal of Engineering for Industry
Research Papers
Analysis of Radiation-Induced Embrittlement Gradients on Fracture Characteristics of Thick-Walled Pressure Vessel Steels
F. J. Loss,
F. J. Loss
Metallurgy Division, Naval Research Laboratory, Washington, D. C.
Search for other works by this author on:
J. R. Hawthorne,
J. R. Hawthorne
Metallurgy Division, Naval Research Laboratory, Washington, D. C.
Search for other works by this author on:
C. Z. Serpan, Jr.,
C. Z. Serpan, Jr.
Metallurgy Division, Naval Research Laboratory, Washington, D. C.
Search for other works by this author on:
P. P. Puzak
P. P. Puzak
Metallurgy Division, Naval Research Laboratory, Washington, D. C.
Search for other works by this author on:
F. J. Loss
Metallurgy Division, Naval Research Laboratory, Washington, D. C.
J. R. Hawthorne
Metallurgy Division, Naval Research Laboratory, Washington, D. C.
C. Z. Serpan, Jr.
Metallurgy Division, Naval Research Laboratory, Washington, D. C.
P. P. Puzak
Metallurgy Division, Naval Research Laboratory, Washington, D. C.
J. Eng. Ind. Nov 1971, 93(4): 1007-1015
Published Online: November 1, 1971
Article history
Received:
January 28, 1971
Online:
July 15, 2010
Citation
Loss, F. J., Hawthorne, J. R., Serpan, C. Z., Jr., and Puzak, P. P. (November 1, 1971). "Analysis of Radiation-Induced Embrittlement Gradients on Fracture Characteristics of Thick-Walled Pressure Vessel Steels." ASME. J. Eng. Ind. November 1971; 93(4): 1007–1015. https://doi.org/10.1115/1.3428036
Download citation file:
Get Email Alerts
Cited By
On-Orbit Processing and Hardware Performance of Microgravity Hydrothermal Synthesis for Graphene Aerogel
J. Manuf. Sci. Eng (December 2024)
A Review on Metallic Drilling Burrs: Geometry, Formation, and Effect on the Mechanical Strength of Metallic Assemblies
J. Manuf. Sci. Eng (April 2025)
Related Articles
Fracture Safety Analysis Concepts for Nuclear Pressure Vessels, Considering the Effects of Irradiation
J. Basic Eng (June,1971)
Heavy-Section Steel Technology and Irradiation Programs—Retrospective and Prospective Views
J. Pressure Vessel Technol (December,2010)
Modeling of Irradiation Embrittlement of Reactor Pressure Vessel Steels
J. Eng. Mater. Technol (January,2000)
Related Chapters
Long.Term Reactivity Change and Control: On.Power Refuelling
Fundamentals of CANDU Reactor Physics
A Study of Irradiation-Induced Growth of Modified and Advanced Zr-Nb System Alloys after Irradiation in the VVER-1000 Reactor Core at Temelin NPP
Zirconium in the Nuclear Industry: 20th International Symposium
Lessons Learned: NRC Experience
Continuing and Changing Priorities of the ASME Boiler & Pressure Vessel Codes and Standards